ELASTOSIL RT622 A+B 1KG 908-52115 WACKER
Виробник: WACKERCategory: Encapsulating materials
Description: Silicone encapsulating compound; brown; 12000mPas; 1kg
Type of chemical agent: silicone encapsulating compound
Colour: brown
Application: sealing and tightening
Shore hardness: 27
Kind of package: can
Elongation at rupture: 550%
Tensile strength: 6.5N/mm2
Weight mixing ratio: 9:1
Dynamic viscosity: 12000mPas
Agent features: excellent heat stability; fast-curing; low viscosity; two-component; very low contraction while curing
Curing method: RTV
Net weight: 1kg
Bonding time: 60min
кількість в упаковці: 1 шт
товар відсутній
Відгуки про товар
Написати відгук
Технічний опис ELASTOSIL RT622 A+B 1KG 908-52115 WACKER
Category: Encapsulating materials, Description: Silicone encapsulating compound; brown; 12000mPas; 1kg, Type of chemical agent: silicone encapsulating compound, Colour: brown, Application: sealing and tightening, Shore hardness: 27, Kind of package: can, Elongation at rupture: 550%, Tensile strength: 6.5N/mm2, Weight mixing ratio: 9:1, Dynamic viscosity: 12000mPas, Agent features: excellent heat stability; fast-curing; low viscosity; two-component; very low contraction while curing, Curing method: RTV, Net weight: 1kg, Bonding time: 60min, кількість в упаковці: 1 шт.
Інші пропозиції ELASTOSIL RT622 A+B 1KG 908-52115
| Фото | Назва | Виробник | Інформація |
Доступність |
Ціна без ПДВ |
|---|---|---|---|---|---|
| ELASTOSIL RT622 A+B 1KG 908-52115 | Виробник : WACKER |
Category: Encapsulating materials Description: Silicone encapsulating compound; brown; 12000mPas; 1kg Type of chemical agent: silicone encapsulating compound Colour: brown Application: sealing and tightening Shore hardness: 27 Kind of package: can Elongation at rupture: 550% Tensile strength: 6.5N/mm2 Weight mixing ratio: 9:1 Dynamic viscosity: 12000mPas Agent features: excellent heat stability; fast-curing; low viscosity; two-component; very low contraction while curing Curing method: RTV Net weight: 1kg Bonding time: 60min |
товар відсутній |