RT625 908-52155 WACKER
Виробник: WACKER
Category: Encapsulating materials
Description: Silicone encapsulating compound; half-transparent; 12000mPas
Type of chemical agent: silicone encapsulating compound
Colour: half-transparent
Application: sealing and tightening
Shore hardness: 25
Kind of package: can
Elongation at rupture: 600%
Density: 1.1g/cm3 @ 20°C
Tensile strength: 6.5N/mm2
Weight mixing ratio: 9:1
Dynamic viscosity: 12000mPas
Agent features: two-component; very low contraction while curing
Curing method: RTV
Net weight: 1kg
Bonding time: 60min
кількість в упаковці: 1 шт
Category: Encapsulating materials
Description: Silicone encapsulating compound; half-transparent; 12000mPas
Type of chemical agent: silicone encapsulating compound
Colour: half-transparent
Application: sealing and tightening
Shore hardness: 25
Kind of package: can
Elongation at rupture: 600%
Density: 1.1g/cm3 @ 20°C
Tensile strength: 6.5N/mm2
Weight mixing ratio: 9:1
Dynamic viscosity: 12000mPas
Agent features: two-component; very low contraction while curing
Curing method: RTV
Net weight: 1kg
Bonding time: 60min
кількість в упаковці: 1 шт
товар відсутній
Відгуки про товар
Написати відгук
Технічний опис RT625 908-52155 WACKER
Category: Encapsulating materials, Description: Silicone encapsulating compound; half-transparent; 12000mPas, Type of chemical agent: silicone encapsulating compound, Colour: half-transparent, Application: sealing and tightening, Shore hardness: 25, Kind of package: can, Elongation at rupture: 600%, Density: 1.1g/cm3 @ 20°C, Tensile strength: 6.5N/mm2, Weight mixing ratio: 9:1, Dynamic viscosity: 12000mPas, Agent features: two-component; very low contraction while curing, Curing method: RTV, Net weight: 1kg, Bonding time: 60min, кількість в упаковці: 1 шт.
Інші пропозиції RT625 908-52155
Фото | Назва | Виробник | Інформація |
Доступність |
Ціна без ПДВ |
---|---|---|---|---|---|
RT625 908-52155 | Виробник : WACKER |
Category: Encapsulating materials Description: Silicone encapsulating compound; half-transparent; 12000mPas Type of chemical agent: silicone encapsulating compound Colour: half-transparent Application: sealing and tightening Shore hardness: 25 Kind of package: can Elongation at rupture: 600% Density: 1.1g/cm3 @ 20°C Tensile strength: 6.5N/mm2 Weight mixing ratio: 9:1 Dynamic viscosity: 12000mPas Agent features: two-component; very low contraction while curing Curing method: RTV Net weight: 1kg Bonding time: 60min |
товар відсутній |